塑胶原料 > 产品分类 > PA12塑胶原料

PA12法国阿科玛3533

PA12法国阿科玛3533

2021-07-07

Physical Properties Metric Comments Density  0.820 - 11.0 g/cc Average value: 1.37 g/cc Grade Count:483 Filler Content  10.0 - 50.0 % Average value: 30.8 % Grade Count:21 Water Absorption  0.0500 - 3.50 % Average value: 1.06 % Grade Count:191 1.65 - 1.90 % Average value: 1.79 % Grade Count:20 @Temperature 100 - 100 °C Moisture Absorption at Equilibrium  0.000 - 2.00 % Average value: 0.660 % Grade Count:212 Water Absorption at Saturation  0.100 - 3.00 % Average value: 1.34 % Grade Count:68 Additive Loading  2.00 - 30.0 % Average value: 19.6 % Grade Count:9 Particle Size  4.00 - 100 µm Average value: 46.4 µm Grade Count:31 pH  4.00 - 6.00 Average value: 4.25 Grade Count:8 Specific Surface Area  1.00 - 9.00 m²/g Average value: 2.44 m²/g Grade Count:8 Viscosity Number  100 - 190 cm³/g Average value: 169 cm³/g Grade Count:9 Maximum Moisture Content  0.0200 - 0.200 Average value: 0.142 Grade Count:8 Thickness  140 - 660 microns Average value: 450 microns Grade Count:3 Linear Mold Shrinkage  0.000200 - 0.0200 cm/cm Average value: 0.00700 cm/cm Grade Count:261 Linear Mold Shrinkage, Transverse  0.000500 - 0.0200 cm/cm Average value: 0.00937 cm/cm Grade Count:180 Melt Flow  0.400 - 190 g/10 min Average value: 29.3 g/10 min Grade Count:99 Mechanical Properties Metric Comments Hardness, Rockwell R  55.0 - 120 Average value: 103 Grade Count:31 Hardness, Shore D  40.0 - 88.0 Average value: 71.3 Grade Count:139 Ball Indentation Hardness  20.0 - 230 MPa Average value: 114 MPa Grade Count:82 Tensile Strength, Ultimate  1.00 - 827 MPa Average value: 76.2 MPa Grade Count:335 15.0 - 110 MPa Average value: 58.4 MPa Grade Count:4 @Temperature 60.0 - 150 °C Tensile Strength, Yield  9.50 - 170 MPa Average value: 44.7 MPa Grade Count:339 Elongation at Break  0.350 - 400 % Average value: 58.1 % Grade Count:518 4.50 - 16.0 % Average value: 8.68 % Grade Count:3 @Temperature 60.0 - 150 °C Elongation at Yield  1.50 - 45.0 % Average value: 12.0 % Grade Count:201 >= 10.0 % Average value: 10.0 % Grade Count:1 @Temperature 60.0 - 150 °C Modulus of Elasticity  0.0800 - 64.1 GPa Average value: 4.69 GPa Grade Count:378 0.259 - 7.20 GPa Average value: 3.29 GPa Grade Count:4 @Temperature 40.0 - 150 °C Tenacity  0.297 - 0.545 N/tex Average value: 0.413 N/tex Grade Count:3 Flexural Yield Strength  5.45 - 607 MPa Average value: 109 MPa Grade Count:159 Flexural Modulus  0.190 - 51.7 GPa Average value: 5.12 GPa Grade Count:189 0.275 - 0.685 GPa Average value: 0.450 GPa Grade Count:1 @Temperature 60.0 - 120 °C Compressive Yield Strength  6.00 - 167 MPa Average value: 69.7 MPa Grade Count:6 Poissons Ratio  0.350 - 0.430 Average value: 0.393 Grade Count:3 0.450 - 0.450 Average value: 0.450 Grade Count:1 @Temperature 100 - 100 °C Izod Impact, Notched  0.160 - 100 J/cm Average value: 2.26 J/cm Grade Count:159 0.210 - 1.10 J/cm Average value: 0.410 J/cm Grade Count:5 @Temperature -40.0 - -20.0 °C Izod Impact, Unnotched  0.0166 J/cm - NB Average value: 12.8 J/cm Grade Count:77 Izod Impact, Notched (ISO)  1.00 - 100000 kJ/m² Average value: 13.6 kJ/m² Grade Count:35 Izod Impact, Unnotched (ISO)  8.00 kJ/m² - NB Average value: 48.4 kJ/m² Grade Count:29 Charpy Impact Unnotched  0.500 J/cm² - NB Average value: 6.70 J/cm² Grade Count:257 3.40 J/cm² - NB Average value: 7.51 J/cm² Grade Count:220 @Temperature -40.0 - 0.000 °C Charpy Impact, Notched  0.100 J/cm² - NB Average value: 2.14 J/cm² Grade Count:258 0.100 J/cm² - NB Average value: 0.962 J/cm² Grade Count:223 @Temperature -40.0 - 0.000 °C Falling Dart Impact  9.73 - 13.0 J Average value: 11.2 J Grade Count:3 Instrumented Impact Total Energy  3.61 - 21.3 J Average value: 12.8 J Grade Count:7 Puncture Energy  53.0 - 70.0 J Average value: 60.6 J Grade Count:5 @Temperature -30.0 - -30.0 °C Instrumented Impact Energy at Peak  5.00 - 13.0 J Average value: 9.67 J Grade Count:6 Coefficient of Friction  0.0200 - 0.670 Average value: 0.303 Grade Count:15 Coefficient of Friction, Static  0.140 - 0.520 Average value: 0.287 Grade Count:8 Tensile Creep Modulus, 1 hour  310 - 1300 MPa Average value: 833 MPa Grade Count:8 Tensile Creep Modulus, 1000 hours  60.0 - 800 MPa Average value: 388 MPa Grade Count:12 Tear Strength Test  0.200 - 52.0 Average value: 19.1 Grade Count:3 K (wear) Factor  15.0 - 898 x 10-8 mm³/N-M Average value: 152 x 10-8 mm³/N-M Grade Count:7 Taber Abrasion, mg/1000 Cycles  1.00 - 18.3 Average value: 1.82 Grade Count:21 Tangent Modulus  1440 - 12800 MPa Average value: 8220 MPa Grade Count:11 Hydrostatic Design Basis  13.7895 - 13.7895 MPa Average value: 13.8 MPa Grade Count:1 @Temperature 60.0 - 60.0 °C Electrical Properties Metric Comments Electrical Resistivity  1.00 - 1.00e+16 ohm-cm Average value: 2.45e+14 ohm-cm Grade Count:278 Surface Resistance  10.0 - 5.20e+15 ohm Average value: 1.39e+14 ohm Grade Count:209 Insulation Resistance  10.0 - 1.00e+9 ohm Average value: 1.02e+8 ohm Grade Count:10 Static Decay  0.00200 - 2.00 sec Average value: 1.50 sec Grade Count:4 Dielectric Constant  2.00 - 17.0 Average value: 4.80 Grade Count:98 Dielectric Strength  1.00 - 100 kV/mm Average value: 37.7 kV/mm Grade Count:208 Dissipation Factor  0.000304 - 0.330 Average value: 0.0819 Grade Count:81 Dielectric Loss Index  0.000200 - 0.0400 Average value: 0.0295 Grade Count:4 Comparative Tracking Index  60.0 - 600 V Average value: 580 V Grade Count:161 Thermal Properties Metric Comments CTE, linear  9.00 - 414 µm/m-°C Average value: 105 µm/m-°C Grade Count:259 100 - 292 µm/m-°C Average value: 196 µm/m-°C Grade Count:2 @Temperature 50.0 - 160 °C CTE, linear, Transverse to Flow  10.6 - 210 µm/m-°C Average value: 118 µm/m-°C Grade Count:133 84.0 - 84.0 µm/m-°C Average value: 84.0 µm/m-°C Grade Count:1 @Temperature 60.0 - 100 °C Specific Heat Capacity  1.38 - 2.50 J/g-°C Average value: 2.16 J/g-°C Grade Count:30 1.68 - 20.3 J/g-°C Average value: 5.28 J/g-°C Grade Count:2 @Temperature 50.0 - 150 °C Thermal Conductivity  0.140 - 37.0 W/m-K Average value: 3.06 W/m-K Grade Count:52 Melting Point  130 - 356 °C Average value: 178 °C Grade Count:300 Maximum Service Temperature, Air  70.0 - 160 °C Average value: 120 °C Grade Count:114 Deflection Temperature at 0.46 MPa (66 psi)  45.0 - 193 °C Average value: 135 °C Grade Count:287 Deflection Temperature at 1.8 MPa (264 psi)  10.0 - 190 °C Average value: 99.6 °C Grade Count:332 Deflection Temperature at 8.0 MPa  40.0 - 160 °C Average value: 111 °C Grade Count:36 Vicat Softening Point  60.0 - 190 °C Average value: 152 °C Grade Count:127 Minimum Service Temperature, Air  -100 - -40.0 °C Average value: -56.7 °C Grade Count:9 Glass Transition Temp, Tg  41.0 - 170 °C Average value: 136 °C Grade Count:21 UL RTI, Electrical  110 - 120 °C Average value: 115 °C Grade Count:4 UL RTI, Mechanical with Impact  70.0 - 85.0 °C Average value: 77.5 °C Grade Count:4 UL RTI, Mechanical without Impact  95.0 °C Average value: 95.0 °C Grade Count:4 Flammability, UL94  HB - V-0 Grade Count:238 Oxygen Index  20.0 - 26.0 % Average value: 22.2 % Grade Count:19 Optical Properties Metric Comments Transmission, Visible  80.0 - 90.0 % Average value: 87.8 % Grade Count:23 Processing Properties Metric Comments Processing Temperature  40.0 - 266 °C Average value: 229 °C Grade Count:101 Die Temperature  230 °C Average value: 230 °C Grade Count:83 Melt Temperature  180 - 288 °C Average value: 223 °C Grade Count:190 Mold Temperature  30.0 - 149 °C Average value: 68.7 °C Grade Count:155 Injection Velocity  100 mm/sec Average value: 100 mm/sec Grade Count:34 Die Opening  0.0400 cm Average value: 0.0400 cm Grade Count:83 Roll Temperature  50.0 °C Average value: 50.0 °C Grade Count:83 Drying Temperature  54.4 - 130 °C Average value: 93.4 °C Grade Count:158 Moisture Content  0.0200 - 1.00 %


价格:80.00元/KG
立即购买
点击这里给我发消息 点击这里给我发消息