PEEK 耐化学 抗疲劳 热稳定 高强度 耐高温 PAEK 美国苏威 AV-621 GF30
价格：59600每吨
Solvay Specialty Polymers AvaSpire® AV-651 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
Material Notes: AvaSpire® AV-651 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-651. This formulation offers some advantages relative to 30% carbon fiber reinforced PEEK which include better dimensional stability and warp resistance during injection molding. The AV-651 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-651-based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK. Those attributes include chemical resistance, fatigue resistance, and long term thermal oxidative stability.
Features: Autoclave Sterilizable; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Sterilizability; Heat Sterilizable; High Heat Resistance; High Stiffness; High Strength; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam Sterilizable
Uses: Dental Applications; Hospital Goods; Medical Devices; Medical/Healthcare Applications; Pump Parts; Seals; Surgical Instruments
Injection Molding Notes: Back Pressure: Minimum
Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Filler Content | 0.3 | 0.3 | Carbon Fiber |
| Water Absorption | 0.002 | 0.002 | ISO 62 |
| @Time 86400 sec | @Time 24.0 hour | ||
| Viscosity | 540000 cP | 540000 cP | Melt Viscosity; ASTM D3835 |
| @Shear Rate 1000 1/s, | @Shear Rate 1000 1/s, | ||
| Temperature 400 °C | Temperature 752 °F | ||
| Linear Mold Shrinkage, Flow | 0.00 - 0.0020 cm/cm | 0.00 - 0.0020 in/in | |
| @Thickness 3.18 mm | @Thickness 0.125 in | ||
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | ASTM D955 |
| @Thickness 3.18 mm | @Thickness 0.125 in | ||
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | ASTM D1238 |
| @Load 2.16 kg, | @Load 4.76 lb, | ||
| Temperature 400 °C | Temperature 752 °F | ||
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 104 | 104 | ASTM D785 |
| Tensile Strength | 184 MPa | 26700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 192 MPa | 27800 psi | 5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 0.015 | 0.015 | Type 1A, 5 mm/min; ISO 527-2 |
| 0.015 | 0.015 | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 20.7 GPa | 3000 ksi | 5 mm/min; ASTM D638 |
| 21.1 GPa | 3060 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| 280 MPa | 40600 psi | ISO 178 | |
| Flexural Modulus | 17.2 GPa | 2490 ksi | ASTM D790 |
| 19.1 GPa | 2770 ksi | ISO 178 | |
| Compressive Strength | 168 MPa | 24400 psi | ASTM D695 |
| Shear Strength | 94.0 MPa | 13600 psi | ASTM D732 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.90 J/cm | 11.1 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.40 kJ/m² | 4.00 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 8.20 µm/m-°C | 4.56 µin/in-°F | 1 |
| @Temperature -50.0 - 50.0 °C | @Temperature -58.0 - 122 °F | ||
| Specific Heat Capacity | 1.32 J/g-°C | 0.315 BTU/lb-°F | ASTM C351 |
| @Temperature 50.0 °C | @Temperature 122 °F | ||
| 1.77 J/g-°C | 0.423 BTU/lb-°F | ASTM C351 | |
| @Temperature 200 °C | @Temperature 392 °F | ||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 345 °C | 653 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Annealed; ASTM D648 |
| @Thickness 3.20 mm | @Thickness 0.126 in | ||
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 366 - 388 °C | 691 - 730 °F | |
| Mold Temperature | 149 - 177 °C | 300 - 351 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| @Time 14400 sec | @Time 4.00 hour | ||
| Descriptive Properties | |||
| Availability | Africa & Middle East | ||
| Asia Pacific | |||
| Europe | |||
| Latin America | |||
| North America | |||
| Color | Black | ||
| Form | Pellets | ||
| Injection Rate | Fast | ||
| Processing Technique | Injection Molding; Machining; Profile Extrusion | ||
| RoHS Compliance | RoHS Compliant | ||
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |