塑胶原料 > 产品分类 > ABS塑胶原料 > 一般级

PA-707塑胶原料

PA-707塑胶原料

2015-12-18

品  名: ABS 707C塑胶原料
单  价: 9.9 RMB/KG
最小起订: 25KG 
供货总量: 100000000
发货期限: 自买家付款之日起 1 天内发货
联 系 人: 王先生
公司电话: 0769-87190386/13662834186
即时通讯: qq:249911599. 微信:ydsujiao
保障.jpg

PA-707 原板技术中英文介绍:
PA-707 General  
Material Status  •Commercial: Active
 
Literature 1  •Processing (English)
 •Technical Datasheet - ASTM (English)
 •Technical Datasheet - ISO (English) 
UL Yellow Card 2  •E56070-245704 
RoHS Compliance  •RoHS Compliant
Processing Method  •Injection Molding
Physical Nominal Value Unit Test Method
Specific Gravity      
-- 1.06 g/cm³ ASTM D792
23°C 1.06 g/cm³ ISO 1183
Melt Mass-Flow Rate (MFR)     ASTM D1238
200°C/5.0 kg 1.7 g/10 min  
220°C/10.0 kg 23 g/10 min  
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) 23.0 cm³/10min ISO 1133
Hardness Nominal Value Unit Test Method
Rockwell Hardness (R-Scale) 116   ASTM D785
Ball Indentation Hardness (H 358/30) 115 MPa ISO 2039-1

Mechanical Nominal Value Unit Test Method
Tensile Stress      
Yield 56.0 MPa ISO 527-2/50
Break 38.0 MPa ISO 527-2/50
3.00 mm 3 48.1 MPa ASTM D638
Tensile Elongation      
Break, 3.00 mm 3 20 % ASTM D638
Break 20 % ISO 527-2/50
Flexural Modulus      
6.00 mm 4 2840 MPa ASTM D790
-- 5 2300 MPa ISO 178
Flexural Strength      
6.00 mm 4 84.3 MPa ASTM D790
-- 5 79.0 MPa ISO 178
Impact Nominal Value Unit Test Method
Charpy Notched Impact Strength 15 kJ/m² ISO 179
Charpy Unnotched Impact Strength No Break   ISO 179
Notched Izod Impact      
23°C, 3.00 mm 160 J/m ASTM D256
23°C, 6.00 mm 140 J/m ASTM D256
-- 13 kJ/m² ISO 180/1A
Unnotched Izod Impact Strength 50 kJ/m² ISO 180/1U

Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load      
1.8 MPa, Unannealed 85.0 °C ASTM D648
1.8 MPa, Unannealed 88.0 °C ISO 75-2/A
1.8 MPa, Annealed 95.0 °C ASTM D648
1.8 MPa, Annealed 98.0 °C ISO 75-2/A
Vicat Softening Temperature      
-- 105 °C ASTM D1525 6
-- 104 °C ISO 306/A50
-- 100 °C ISO 306/B50

Flammability Nominal Value   Test Method
Flame Rating (1.60 mm) HB   UL 94

Injection Nominal Value Unit  
Drying Temperature 80.0 to 85.0 °C  
Drying Time 2.0 to 4.0 hr  
Rear Temperature 180 to 220 °C  
Middle Temperature 190 to 230 °C  
Front Temperature 190 to 230 °C  
Mold Temperature 30.0 to 70.0 °C  

Notes
1These links provide you with access to supplier literature. We work hard to keep them up to date; however you may find the most current literature from the supplier.
2A UL Yellow Card contains UL-verified flammability and electrical characteristics. UL IDES continually works to link Yellow Cards to individual plastic materials in Prospector, however this list may not include all of the appropriate links. It is important that you verify the association between these Yellow Cards and the plastic material found in Prospector. For a complete listing of Yellow Cards, visit the UL Yellow Card Search.
36.0 mm/min
42.8 mm/min
52.0 mm/min
6Rate A (50°C/h)

总体   
资料 1  •Processing (English)
 •Technical Datasheet - ASTM (English)
 •Technical Datasheet - ISO (English)
UL 黄卡 2  •E56070-245704 
RoHS 合规性  •RoHS 合规
加工方法  •注射成型
物理性能 额定值 单位制 测试方法
比重      
-- 1.06 g/cm³ ASTM D792
23°C 1.06 g/cm³ ISO 1183
熔流率     ASTM D1238
200°C/5.0 kg 1.7 g/10 min  
220°C/10.0 kg 23 g/10 min  
溶化体积流率(MVR) (220°C/10.0 kg) 23.0 cm³/10min ISO 1133
硬度 额定值 单位制 测试方法
洛氏硬度 (R 计秤) 116   ASTM D785
球压硬度 (H 358/30) 115 MPa ISO 2039-1

机械性能 额定值 单位制 测试方法
拉伸应力      
屈服 56.0 MPa ISO 527-2/50
断裂 38.0 MPa ISO 527-2/50
3.00 mm 3 48.1 MPa ASTM D638
伸长率      
断裂, 3.00 mm 3 20 % ASTM D638
断裂 20 % ISO 527-2/50
弯曲模量      
6.00 mm 4 2840 MPa ASTM D790
-- 5 2300 MPa ISO 178
弯曲强度      
6.00 mm 4 84.3 MPa ASTM D790
-- 5 79.0 MPa ISO 178
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度 15 kJ/m² ISO 179
简支梁缺口冲击强度 无断裂   ISO 179
悬壁梁缺口冲击强度      
23°C, 3.00 mm 160 J/m ASTM D256
23°C, 6.00 mm 140 J/m ASTM D256
-- 13 kJ/m² ISO 180/1A
无缺口伊佐德冲击强度 50 kJ/m² ISO 180/1U

热性能 额定值 单位制 测试方法
热变形温度      
1.8 MPa, 未退火 85.0 °C ASTM D648
1.8 MPa, 未退火 88.0 °C ISO 75-2/A
1.8 MPa, 退火 95.0 °C ASTM D648
1.8 MPa, 退火 98.0 °C ISO 75-2/A
维卡软化温度      
-- 105 °C ASTM D1525 6
-- 104 °C ISO 306/A50
-- 100 °C ISO 306/B50

可燃性 额定值   测试方法
UL 阻燃等级 (1.60 mm) HB   UL 94

注射 额定值 单位制  
干燥温度 80.0 到 85.0 °C  
干燥时间 2.0 到 4.0 hr  
螺筒后部温度 180 到 220 °C  
螺筒中部温度 190 到 230 °C  
螺筒前部温度 190 到 230 °C  
模具温度 30.0 到 70.0 °C  

备注
1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。
 
3  6.0 mm/min
4  2.8 mm/min
5  2.0 mm/min
6  标准 A (50°C/h)
 


:0.00元/
立即购买